Li Wang^1,2,#, Rongbai Tong^3,#, Juanli Wang^1,2,*, Jintao Wan^1,2,*, Yuhu Li^1,2, Pujun Jin^1,2, Daodao Hu^1,2

Journal of Renewable Materials, Vol.10, No.5, pp. 1349-1364, 2022, DOI:10.32604/jrm.2022.019372

Abstract Quest for bio-based halogen-free green flame retardant has attracted many concerns in recent years. Herein a reactive functional flame retardant containing phosphorus VDP is synthesized from vanillin, 9,10-dihydro-9-oxa-10-phosphophene-10-oxide (DOPO) and phenol via a facile way. VDP is characterized with ¹H NMR, ³¹P NMR, FTIR and Time of Flight Mass Spectrometry, and used as a new reactive flame retardant for bisphenol epoxy thermosets. Thermogravimetry analysis shows that when the VDP loading is only 0.5P% (based on phosphorus content), the residue increases from 14.2% to 21.1% at 750°C in N₂ compare with neat DGEBA. Correspondingly, the limit oxygen index increased to 29.6%,… More >

Bing Zhang¹, Sujie Yang¹, Mengru Liu¹, Panyue Wen², Xiuyu Liu¹, Gang Tang^1,*, Xiangrong Xu^3,4,*

Journal of Renewable Materials, Vol.10, No.5, pp. 1201-1220, 2022, DOI:10.32604/jrm.2022.018047

Abstract Biomass phytic acid has potential flame retardant value as the main form of phosphorus in plant seeds. In this study, phytate-based flame retardants aluminum phytate (PA-Al) and iron phytate (PA-Fe) were synthesized and characterized. Subsequently, they were introduced into rigid polyurethane foam (RPUF) as flame retardants by one-step water-blown method. The results indicated that RPUF/PA-Fe30 exhibited the highest char residue of 22.1 wt%, significantly higher than 12.4 wt% of RPUF. Cone calorimetry analysis showed that the total heat release (THR) of RPUF/PA-Al30 decreased by 17.0% and total smoke release (TSR) decreased by 22.0% compared with pure RPUF, which were the lowest, demonstrating… More > Graphic Abstract

Qionglin Luo¹, Mingliang Wang², Hui Zhang¹, Yuejun Ouyang¹, Hongwei Lin¹, You Shu^1,*, Shengpei Su^1,2,*

Journal of Renewable Materials, Vol.9, No.12, pp. 2067-2076, 2021, DOI:10.32604/jrm.2021.016255

Abstract Poly(L-lactic acid) (PLLA) is a thermoplastic material with complete degradability, high biocompatibility and excellent mechanical properties. It can replace petroleum-based polymers are currently being used in the fields of packaging, agriculture, textiles, medical and so on. However, PLLA’s extremely flammability greatly limits its wider application. An bio-based flame retardant L-APP/PLLA composites was prepared by melt blending of the L-APP and PLLA. The morphology, impact properties, thermal properties and flame retardant properties of composites were investigated by field emission scanning electron microscope (SEM), impact tester, differential scanning calorimeter (DSC), thermogravimetric analyzer (TGA), limiting oxygen indexer (LOI) and horizontalvertical burning tester. The… More > Graphic Abstract

You Shu^1,2, Qionglin Luo², Hongwei Lin^2,*, Yuejun Ouyang², Xiaomin Zhang^1,2, Liping Sheng¹, Shengpei Su^1,2,*

Journal of Renewable Materials, Vol.9, No.5, pp. 909-921, 2021, DOI:10.32604/jrm.2021.014216

Abstract Polyvinyl alcohol (PVA) has been widely used in the fields of medical, food and packaging due to its excellent biocompatibility, good fiber-forming and film-forming properties. However, the high flammability of PVA has greatly limited its wider applications. The flame-retardant PVA was prepared by melt blending of a bio-based flame retardant (prepared from lignin, phosphoric acid and carbamide) with thermoplastic PVA (TPVA). The chemical structure, morphology, thermal properties, mechanical properties, fire property and fluidity of this flame retardant PVA were investigated by Fourier transform infrared spectrometer(FTIR), field emission scanning electron microscope(SEM), thermogravimetric analyzer(TGA), impact tester, universal testing machine, horizontal-vertical burning tester,… More >

Fouad LAOUTID^1,*, Valeriia KARASEVA¹, Lucie COSTES^{1, 2}, Sylvain BROHEZ², Rosica MINCHEVA¹, Philippe DUBOIS¹

Journal of Renewable Materials, Vol.6, No.6, pp. 559-572, 2018, DOI:10.32604/JRM.2018.00004

Abstract In this study, tannic acid (TA) was investigated as flame retardant agent for PLA. Different strategies to modify its thermal degradation pathway have been explored in order to improve its charring effect. The first one consists in combining TA with organomodified montmorillonite (oMMT), and enables limiting the thermo-oxidative degradation of TA and promoting the formation of an effective char layer. Flame-retardant (FR) behavior of PLA-based composition has been found to be positively impacted by this combination since a reduction of the peak of Heat Release Rate (PHRR), more important than the value recorded when oMMT and tannic acid are used… More >