CMC-Computers, Materials & Continua, Vol.8, No.1, pp. 33-42, 2008, DOI:10.3970/cmc.2008.008.033
Abstract Thermal cycling degradation effect on tensile and flexural properties of Cytec T650 carbon/Lonza Primaset PT-30 cyanate ester composite rods used for gas turbine engine brush seals was evaluated. The composite rods were thermal cycled in air from room temperature to 315°C for 100, 200, 400, 600 and 800 cycles. Each thermal cycle is a one hour period with 28 minutes hold at peak temperature and a high heating/cooling rate of 73°C/min. The composite withstood the first 100 thermal cycles with less than 10% property change. After that, tensile strength and fracture strain as well as flexural modulus were gradually reduced.… More >