Jingjing Liao^1,2, Jinxing Li², Fuxian Yang², Yan Zhu², Hongyan Wang³, Guanben Du^1,2,*, Hisham Essawy⁴, Xiaojian Zhou^2,*

Journal of Renewable Materials, Vol.10, No.2, pp. 359-372, 2022, DOI:10.32604/jrm.2021.016335

Abstract Polyvinyl alcohol (PVA)-based films containing Chinese bayberry tannin (BT) were prepared by cross-linking using glyoxal, glutaraldehyde and dialdehyde starch, individually. The presence of cross-linkers was evident to promote the transparency and decrease the moisture content of PVA/BT films, while the water solubility stayed almost unchanged in the cross-linked PVA/BT films. All cross-linkers provided promotion of the water vapor permeability, mechanical property and thermal stability of PVA/BT films. The best water vapor barrier capacity was found in case of glutaraldehyde cross-linked PVA/BT film, while the highest tensile strength was encountered in case of glyoxal cross-linked PVA/BT films, compared with the uncross-linked… More > Graphic Abstract

Xiaoliang Zhao^1,#, Yuting Wang^1,#, Xiuying Pu¹, Jianzhong Ma¹, Feifan Leng¹, Yonggang Wang¹, Yanling Wang¹, Shuhong Yang¹, Fen Ran², Weijie Zhang^1,*

Journal of Renewable Materials, Vol.7, No.12, pp. 1321-1332, 2019, DOI:10.32604/jrm.2019.07757

Abstract A series of the Guiqi polysaccharides/chitosan/alginate composite hydrogel microspheres (GPcM) with different particle sizes were prepared with Guiqi polysaccharides (GP), chitosan (CS) and sodium alginate (Alg). The optimum preparation process was also determined by single factor and orthogonal experiment analysis. The GPcM were characterized by fourier transform infrared spectroscopy (FT-IR), scanning electron microscope (SEM), drug loading efficiency test (LE), encapsulation efficiency test (EE) and in vitro release study. The results showed that the Guiqi polysaccharides chitosan hydrogel (GPCH) and sodium alginate hydrogel (SAH) formed a crossover system in GPcM. The GPcM have a uniform particle size ranging from 395.1μm to… More >