Henghui Deng^1,2, Jingyi Lu^1,2, Dunsheng Liang^1,2, Xiaomin Wang^1,2, Tongyao Wang^1,2, Weihao Zhang^1,2, Jing Wang^3,*, Chaoqun Zhang^1,2,*

Journal of Renewable Materials, Vol.11, No.3, pp. 1209-1222, 2023, DOI:10.32604/jrm.2022.023371

Abstract In this study, acrylic acid was used as a neutralizer to prepare bio-based WPU with an interpenetrating polymer network structure by thermally induced free radical emulsion polymerization. The effects of the content of acrylic acid on the properties of the resulting waterborne polyurethane-poly (acrylic acid) (WPU-PAA) dispersion and the films were systematically investigated. The results showed that the cross-linking density of the interpenetrating network polymers was increased and the interlocking structure of the soft and hard phase dislocations in the molecular segments of the double networks was tailored with increasing the content of acrylic acid, leading to enhancement of the… More > Graphic Abstract

Mehul Barde^1,2, Yusuf Celikbag³, Brian Via³, Sushil Adhikari⁴, Maria L. Auad^1,2,*

Journal of Renewable Materials, Vol.6, No.7, pp. 724-736, 2018, DOI:10.32604/JRM.2018.00116

Abstract Bio-based phenol-formaldehyde polymer (BioNovolac) was developed by reacting molar excess of bio-oil/phenol with formaldehyde in acidic medium. Glycidyl 3,5-diglycidoxybenzoate (GDGB), was prepared by direct glycidylation of α-resorcylic acid (RA), a naturally occurring phenolic monomer. GDGB was crosslinked in the presence of BioNovolac by anionic polymerization. Fourier transform infrared spectroscopy (FTIR) confirmed the formation of semi-interpenetrating polymer networks. The glass transition temperature and moduli of bio-based crosslinked systems were observed to increase with increasing GDGB content. Active chain density and mass retention measured by dynamic mechanical analysis (DMA) and Soxhlet extraction, respectively, indicated a high crosslink density of the cured networks.… More >

Bernal Sibaja^1,2,3, Camila Pereira Matheus^1,2, Ricardo Ballestero Mendez^1,2,Ramsis Farag^1,2,4, J. R. Vega-Baudrit³, Maria L. Auad^*,1,2

Journal of Renewable Materials, Vol.5, No.3-4, pp. 241-250, 2017, DOI:10.7569/JRM.2017.634114

Abstract The thermo-mechanical properties and linear fracture mechanics of acrylated soybean oil and the triglycidylated ether of α-resorcylic acid interpenetrated networks as a function of their weight composition are the focus of Part 2 of this article. Thermo-mechanical characterization showed that the obtained materials behave as thermoset amorphous polymers, and that both the modulus and glass transition are extremely dependent on the epoxy/acrylate weight ratio. Modulus values ranged from 0.7 to 3.3 GPa at 30 °C, and glass transition temperatures ranged from around 58 °C to approx. 130 °C. No synergistic effect on these two properties was observed. Interpenetrating networks containing… More >

Bernal Sibaja^1,2,3, Camila Pereira Matheus^1,2, Ricardo Ballestero Mendez^1,2, J. R. Vega-Baudrit³, Maria L. Auad^*,1,2

Journal of Renewable Materials, Vol.5, No.3-4, pp. 231-240, 2017, DOI:10.7569/JRM.2017.634113

Abstract Interpenetrating polymer networks (IPNs) using an epoxy phase synthesized from chemically modified α-resorcylic acid, and an acrylate phase employing acrylated soybean oil are the main focus of this study. Part 1 details the epoxidation of α-resorcylic acid with epichlorohydrin in alkaline medium, as well as the study of the polymerization and network formation of the generated epoxy-acrylate interpenetrated systems. The epoxy content of the epoxidized α-resorcylic acid was measured by means of a titration using HBr in acetic acid solution, and the functionalization was studied by FTIR. From the obtained results, mainly calorimetry and gel time determination, it was clear… More >