Open Access

ARTICLE

Influence of annealing temperature on nano crystalline description for CuZnS thin films

A. J. Soud, Bushra K. H. Al-Maiyaly

Department of physics, College of Education For Pure Science (Ibn Al-Haitham), University of Baghdad, Baghdad, Iraq

* Corresponding Author:

Chalcogenide Letters 2024, 21(5), 385-394. https://doi.org/10.15251/CL.2024.215.385

Received 30 January 2024; Accepted 07 May 2024;

Abstract

Copper Zinc Sulphide (Cu_0.5Zn_0.5S) alloy and thin films were fabricated in a vacuum. Nano crystallized (CZS) film with thick 450±20 nm was deposit at substrates glasses using thermal evaporation technique below ~ 2 × 10⁻⁵ mbar vacuum to investigated the films structural, morphological and optical properties depended on annealing temperatures ( as-deposited, 423, 523 and 623) K for one hour. The influences annealed temperature on structurally besides morphologically characteristics on these films were investigated using XRD and AFM respectively. XRD confirms the formation a mixed hexagonal phase of CuS-ZnS in (102) direction with polycrystalline in nature having very fine crystallites size varying from (5.5-13.09) nm. AFM analysis shows the uniform distribution of closely packed grains, grain size for that film diverge on ranges as of (52.37 to 89.25) nm after annealed. The optical properties of all films prepared had been examined for the wavelength range 400 - 1000 nm using UV-Vis-NIR spectrometer. The band gaps of (Cu_0.5Zn_0.5S) films are obtained in the range of 2.4 to 1.9 eV, which makes it a suitable absorber as well as buffer/window layer for solar cell applications.

---

Keywords

---