Jingjing Liao^1,2, Jinxing Li², Fuxian Yang², Yan Zhu², Hongyan Wang³, Guanben Du^1,2,*, Hisham Essawy⁴, Xiaojian Zhou^2,*

Journal of Renewable Materials, Vol.10, No.2, pp. 359-372, 2022, DOI:10.32604/jrm.2021.016335

Abstract Polyvinyl alcohol (PVA)-based films containing Chinese bayberry tannin (BT) were prepared by cross-linking using glyoxal, glutaraldehyde and dialdehyde starch, individually. The presence of cross-linkers was evident to promote the transparency and decrease the moisture content of PVA/BT films, while the water solubility stayed almost unchanged in the cross-linked PVA/BT films. All cross-linkers provided promotion of the water vapor permeability, mechanical property and thermal stability of PVA/BT films. The best water vapor barrier capacity was found in case of glutaraldehyde cross-linked PVA/BT film, while the highest tensile strength was encountered in case of glyoxal cross-linked PVA/BT films, compared with the uncross-linked… More > Graphic Abstract

Jingjing Liao^1,2, Jinxing Li², Hongyan Wang³, Yan Zhu², Hisham Essawy⁴, Guanben Du^1,2,*, Xiaojian Zhou^2,*

Journal of Renewable Materials, Vol.10, No.1, pp. 19-31, 2022, DOI:10.32604/jrm.2021.016152

Abstract The current work explores the potential use of commercial Chinese bayberry tannin (BT) to develop antioxidant PVA-based films using solvent casting process for packaging applications. The effect of BT concentration on opacity, water resistance and antioxidant capacity of resulting films was investigated. Properties like tensile strength, thermal behavior, and morphological aspects were also characterized. The experimental results showed that PVA/BT films formed with uniformly brown color and generally good transparency, offering good antioxidant ability. The PVA film containing BT presented slightly higher water resistance according to the results of moisture content and water vapor permeability, especially at low BT content… More > Graphic Abstract