Yiwen Zhang¹, Jianjun Xie^1,*, Minghui Sun¹, Shaolong Wang¹, Tengfei Xu^2,3, Yonggen Xu^2,3, Xiaoqing Ding^2,3, Ying Shi¹, Lei Zhang¹

Journal of Renewable Materials, Vol.11, No.5, pp. 2125-2141, 2023, DOI:10.32604/jrm.2023.025127

Abstract Foam glass is a kind of green building material that is widely used because of its excellent thermal insulation and mechanical properties. In this study, the borosilicate foam glass was fabricated by powder sintering method using recycled soda lime waste glass, quartz, and borax as the primary raw materials. CaCO₃ was used as a foaming agent and Na₂CO₃ as a flux agent. Results showed that as the quartz content decreases from 30 to 17.5 wt.% and borax content increases from 5 to 17.5 wt.%, the pore size, porosity, and thermal insulation of borosilicate foam glass increase significantly, while the compressive strength decreases… More > Graphic Abstract

Yang Liu¹, Jianjun Xie^1,*, Peng Hao¹, Ying Shi¹, Yonggen Xu^2,3, Xiaoqing Ding^2,3

Journal of Renewable Materials, Vol.9, No.2, pp. 237-253, 2021, DOI:10.32604/jrm.2021.012228

Abstract Foam glass is a new green material to make use of waste glass and is popular for its energy-saving and light weight features. The problems in the current study of foam glass is that its properties require improvement to match the growing demands of application specific standards. Properties of foam glass is related to its porous structure, which is affected by various factors. The influence of raw material component, foaming agents and sintering system on the porous structure and properties of foamed glass is studied. Density decreases with the decrease of quartz and barite content. Thermal conductivity is more affected… More >