M.R. Khoshravan¹, M. Hosseinzadeh¹

CMES-Computer Modeling in Engineering & Sciences, Vol.45, No.2, pp. 179-206, 2009, DOI:10.3970/cmes.2009.045.179

Abstract A sandwich panel's optimum core height and composite face thickness, under defined loading, have been computed in order to reach the structure's lowest weight and highest stiffness. The Tsai-Hill criterion was used in order to control the support of transverse loading by the panel. Regarding the relationships in the sandwich materials, the studied material was modeled with the MATLAB package. The Genetic Algorithm (GA) that is based on statistics was used. Our goal was to obtain the best methods of the GA in order to present an optimization method for the sandwich structure. Hence, a sensibility analysis was performed. In… More >

Qiuren Ou^1,2,*, Peijun Ji², Jun Xiao¹, Ling Wu²

FDMP-Fluid Dynamics & Materials Processing, Vol.15, No.1, pp. 27-37, 2019, DOI:10.32604/fdmp.2019.04787

Abstract The properties of resin transfer molding (RTM) cyanate ester and its T800 grade carbon fiber composites were studied with the rheometer, differential scanning calorimetry (DSC), FT-IR, dynamic mechanical analyzer (DMA), thermal gravimetric analysis (TGA), mechanical property testing, and scanning electron microscopy (SEM). The results showed that the temperature of cyanate ester suitable for RTM process was 70℃. Curing process of the resin was 130℃/2 h+160℃/2 h+200℃/2 h+220℃/4 h. Glass transition temperature and heat decomposition temperature of the cured resin are 289℃ and 415℃, respectively. Mechanical properties of T800/RTM cyanate composites are 13.5% higher than that of T700/RTM cyanate composites and… More >

Huanchun Chen¹, Kunigal Shivakumar¹

CMC-Computers, Materials & Continua, Vol.8, No.1, pp. 33-42, 2008, DOI:10.3970/cmc.2008.008.033

Abstract Thermal cycling degradation effect on tensile and flexural properties of Cytec T650 carbon/Lonza Primaset PT-30 cyanate ester composite rods used for gas turbine engine brush seals was evaluated. The composite rods were thermal cycled in air from room temperature to 315°C for 100, 200, 400, 600 and 800 cycles. Each thermal cycle is a one hour period with 28 minutes hold at peak temperature and a high heating/cooling rate of 73°C/min. The composite withstood the first 100 thermal cycles with less than 10% property change. After that, tensile strength and fracture strain as well as flexural modulus were gradually reduced.… More >

Shen Yubin¹, Xie Huicai^1,2, Den Wei¹

CMC-Computers, Materials & Continua, Vol.3, No.2, pp. 49-54, 2006, DOI:10.3970/cmc.2006.003.049

Abstract Bonding an overlay of new concrete onto the damaged concrete is a usual repair method. Because of the different shrinkage rate of the new and old concrete, restrained shrinkage cracks will appear in the new concrete. The cracks will reduce durability and strength of the repaired structure. A new repair method using an interface layer of carbon fiber reinforced cement mortar between new and old concrete was developed in this paper. The new method was found to be very effective in reducing shrinkage cracking of repaired beams and slabs. Comparing with normal repaired beams, the maximum observed width of the… More >