Jianping Deng¹, Qianqian Zhang¹, Yuling Lan¹, Lingcong Luo¹, Zimin Dai¹, Zhonghang Lin¹, Zhixin Lu¹, Jiancheng Yuan¹, Yiqi Fu¹, Lu Luo^2,*, Weigang Zhao^1,*

Journal of Renewable Materials, Vol.11, No.6, pp. 2631-2646, 2023, DOI:10.32604/jrm.2023.027163

Abstract The development and utilization of biomass and agroforestry processing byproducts for high-value applications have been an important topic in the field of renewable materials research. Based on this, a two-step microwave hydrothermal pre-carbonization and KOH activation method was proposed to synthesize tannin-based activated carbons with a high specific surface area, hierarchical pore structure, and good electrochemical performance. The microstructure, texture properties, and physicochemical characteristics were investigated. The results show that the prepared tannin-based activated carbons presented a hierarchical pore structure (micro- and mesopores) with a specific surface area as high as 997.46 m³ g⁻¹ . The electrochemical analysis shows that… More > Graphic Abstract

Zun Bi^1,2,3, Ke Jia^1,2,3, Yunfei Liu^1,2,3,*, Yinong Lyu^1,2,3,*

Journal of Renewable Materials, Vol.10, No.2, pp. 431-451, 2022, DOI:10.32604/jrm.2022.016735

Abstract A series of uniform single-phase spherical BaWO₄: Dy³⁺, Tm³⁺, Eu³⁺ phosphors were prepared via a microwave hydrothermal method by using trisodium citrate dehydrate as surfactant. The phase structure, morphology and photoluminescence properties were measured by powder X-ray diffraction, scanning electron microscope and fluorescence spectrometer, respectively. The results show that uniform spherical microcrystals with diameters in the range of 2–4 μm are obtained. And the phase and morphology of samples are not significantly changed by doping rare earth (RE³⁺) ions. Under the excitation wavelength of 356 and 365 nm, the samples BaWO₄: 0.03Dy³⁺, yTm³⁺ can emit cold white light. In order to… More >