Effect of Steam Explosion Technology Main Parameters on Moso Bamboo and Poplar Fiber

Biqing Shu1,2, Qin Ren1, Lu Hong1, Zhongping Xiao2, Xiaoning Lu1,*, Wenya Wang2, Junbao Yu2,Naiqiang Fu2, Yiming Gu2, Jinjun Zheng2

1 The College of Materials Science and Engineering, Nanjing Forestry University, Nanjing, 210037, China
2 College of Civil Engineering, Yangzhou Polytechnic Institute, Yangzhou, 225127, China

* Corresponding Author: Xiaoning Lu. Email: email

(This article belongs to the Special Issue: Polymeric Composites Based on Sustainable Technologies and Renewable Materials)

Journal of Renewable Materials 2021, 9(3), 585-597. https://doi.org/10.32604/jrm.2021.012932

Abstract

One of the large-scale industrial applications of Moso bamboo and poplar in China is the production of standardized fiberboard. When making fiberboard, a steam blasting pretreatment without the addition of traditional adhesives has become increasingly popular because of its environmental friendliness and wide applicability. In this study, the steam explosion pretreatment of Moso bamboo and poplar was conducted. The steam explosion pressure and holding time were varied to determine the influence of these factors on fiber quality by investigating the morphology of the fiber, the mass ratio of the unexploded specimen at the end face, the chemical composition, and the tensile strength. The following conclusions were drawn: as the steam burst pressure and holding time increased, more cellulose and hemicellulose degradation occurred (the degradation of hemicellulose was greater than that of cellulose), the lignin content rose, and the fiber bundle strength decreased. The degradation of bamboo cellulose was slightly higher than that of poplar, and the degradation of poplar hemicellulose was significantly faster than that of bamboo. Furthermore, increasing the steam explosion pressure and pressure holding time could not effectively increase the lignin content. It is recommended to use a steam blasting pressure of 2.5 MPa or 3.0 MPa and a holding time of 180 s to perform steam blasting on bamboo and poplar specimens.

Keywords


Cite This Article

APA Style
Shu, B., Ren, Q., Hong, L., Xiao, Z., Lu, X. et al. (2021). Effect of steam explosion technology main parameters on moso bamboo and poplar fiber. Journal of Renewable Materials, 9(3), 585-597. https://doi.org/10.32604/jrm.2021.012932
Vancouver Style
Shu B, Ren Q, Hong L, Xiao Z, Lu X, Wang W, et al. Effect of steam explosion technology main parameters on moso bamboo and poplar fiber. J Renew Mater. 2021;9(3):585-597 https://doi.org/10.32604/jrm.2021.012932
IEEE Style
B. Shu et al., "Effect of Steam Explosion Technology Main Parameters on Moso Bamboo and Poplar Fiber," J. Renew. Mater., vol. 9, no. 3, pp. 585-597. 2021. https://doi.org/10.32604/jrm.2021.012932

Citations




cc Copyright © 2021 The Author(s). Published by Tech Science Press.
This work is licensed under a Creative Commons Attribution 4.0 International License , which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • 3310

    View

  • 1921

    Download

  • 1

    Like

Share Link