Bernal Sibaja^1,2,3, Camila Pereira Matheus^1,2, Ricardo Ballestero Mendez^1,2, J. R. Vega-Baudrit³, Maria L. Auad^*,1,2

Journal of Renewable Materials, Vol.5, No.3-4, pp. 231-240, 2017, DOI:10.7569/JRM.2017.634113

Abstract Interpenetrating polymer networks (IPNs) using an epoxy phase synthesized from chemically modified α-resorcylic acid, and an acrylate phase employing acrylated soybean oil are the main focus of this study. Part 1 details the epoxidation of α-resorcylic acid with epichlorohydrin in alkaline medium, as well as the study of the polymerization and network formation of the generated epoxy-acrylate interpenetrated systems. The epoxy content of the epoxidized α-resorcylic acid was measured by means of a titration using HBr in acetic acid solution, and the functionalization was studied by FTIR. From the obtained results, mainly calorimetry and gel time determination, it was clear… More >

Facundo I. Altuna¹, Borja Fernández-d’Arlas², M. Angeles Corcuera², Arantxa Eceiza², Mirta I. Aranguren³, Pablo M. Stefani^3*

Journal of Renewable Materials, Vol.4, No.4, pp. 275-284, 2016, DOI:10.7569/JRM.2016.634120

Abstract Mixtures of biomass-derived polyols were used to synthesize rigid polyurethane (PU) foams. A commercial polymerized methylene diphenyl diisocyanate (pMDI) was used as crosslinker, and distilled water served as foaming agent. The morphology and mechanical properties of foams with different glycerol and water contents were compared in order to evaluate the most suitable formulations. The rigid foams with higher water contents had larger and more anisotropic cells, explaining their lower density. Compressive moduli ranged from about 2.5 MPa to above 20 MPa and collapse stresses from 55 kPa to more than 1 MPa for densities between 54 and 143 kg/m3. Densification… More >