A. Ramírez-Jiménez^1*, S. Hernández López¹, E. Bucio², E. Vigueras Santiago¹

Journal of Renewable Materials, Vol.5, No.2, pp. 132-144, 2017, DOI:10.7569/JRM.2016.634138

Abstract Epoxidized linseed oil (ELO) was synthesized and functionalized with propargylamine (PA) or 3-ethynylaniline (EA) and the products were crosslinked to obtain the diacetylene-functionalized epoxidized linseed oil polymers which were used as matrices in the preparation of the composites with multiwalled carbon nanotubes (MWCNTs). Electrical resistance at percentages between 4 and 20 wt/wt% of filler was measured and the percolation threshold was calculated, obtaining 1.2 and 1.7% for the composites with EA and PA respectively. Low critical concentration evidenced a good dispersion of the MWCNTs without necessity of any modification. The final products were used in the sensing of acetone, chloroform… More >

M. Himabindu¹, K. Kamalakar², MSL Karuna², Aruna Palanisamy^1*

Journal of Renewable Materials, Vol.5, No.2, pp. 124-131, 2017, DOI:10.7569/JRM.2016.634137

Abstract Rigid polyurethane biofoams were prepared from karanja polyol which was derived by ring-opening reaction of epoxidized karanja oil. The polyol, which had a hydroxyl value of 186 mg KOH/g, was thoroughly characterized and the structure confirmed by spectral techniques. The foam formulations were developed to achieve shrinkage-free foams with water used as the blowing agent. The resulting foams were characterized for their mechanical properties like density, compression strength and flexural strength. The densities and mechanical properties, such as compression and flexural strength, varied with the amount of methylene diphenyl diisocyanate (MDI) for a fixed amount of polyol and other additives… More >

Mohamed Ammar¹, Ramzi Khiari^2,3,4*, Mohamed Naceur Belgacem^3,4*, Elimame Elaloui¹

Journal of Renewable Materials, Vol.5, No.2, pp. 116-123, 2017, DOI:10.7569/JRM.2016.634136

Abstract The present study investigated the preparation of biomatrices from Stipa tenacissima L. and its valorization for fiberboard application. Resins were produced by extracting lignin from the Stipa tenacissima L. black liquor by soda process and combining it with glyoxal as crosslinking agent to produce lignin-glyoxal-resin (LGR). The matrix was characterized by several methods, such as FTIR and ATG/ATD, and then mixed with date palm rachis as reinforcing fibers in different proportions of 30 and 50% (w/w with respect to the matrix) to produce biodegradable composite materials. Then, their thermal and mechanical properties were determined, using differential scanning calorimetry (DSC) and… More >

F. Luzi¹, E. Fortunati^1*, A. Jiménez², D. Puglia¹, A. Chiralt², L. Torre¹

Journal of Renewable Materials, Vol.5, No.2, pp. 103-115, 2017, DOI:10.7569/JRM.2016.634135

Abstract Poly(lactic acid) (PLA) based nanocomposites reinforced with 1 wt% of surfactant-modified cellulose nanocrystals (s-CNC) extracted from Posidonia oceanica plant waste and zinc oxide nanoparticles (ZnO NPs) at different concentrations (0.1 and 0.5 wt%) were prepared by solvent casting process. Their thermal, morphological, optical, mechanical and water vapor permeability properties were investigated. Tensile testing showed increased values for strength and deformation at break in PLA based formulations reinforced with s-CNC and ZnO NPs as a consequence of better nanofiller dispersion compared to binary films reinforced only with ZnO NPs. Moreover, the effect of s-CNC and ZnO NPs provoked an improvement of… More >

Purnendu, Soumitra Satapathi^*

Journal of Renewable Materials, Vol.5, No.2, pp. 96-102, 2017, DOI:10.7569/JRM.2016.634134

Abstract Graphene-based 3D porous xerogel was designed through molecular self-assembly of graphene oxide on chitosan matrix and its application in removal of different heavy metal ions from wastewater was investigated. The synthesized xerogel was characterized through FTIR, SEM, XRD and BET surface area analysis. Heavy metal ions, including Pb(II), Cd(II), and Hg(II), were removed from wastewater using this graphene-chitosan (GO-Cs) xerogel and the removal efficiency was monitored through inductively coupled plasma mass spectrometry (ICP-MS). The effect of GO-Cs composition and pH on adsorption efficiency as well as the kinetics of adsorption was studied in detail. The study exhibited that this xerogel… More >

Elena Fortunati^1*, Francesca Luzi¹, Chiara Fanali², Laura Dugo², Maria Giovanna Belluomo², Luigi Torre¹, José Maria Kenny¹, Luca Santi³, Roberta Bernini³

Journal of Renewable Materials, Vol.5, No.2, pp. 81-95, 2017, DOI:10.7569/JRM.2016.634132

Abstract Hydroxytyrosol (HTyr), a biophenol found in extra-virgin olive oil or olive oil by-products, well known for its strong antioxidant activity, was used as active ingredient for poly(vinyl alcohol) (PVA) matrix to develop film formulations by solvent casting process. The effect of HTyr on the morphological, thermal stability, optical, mechanical and release properties of PVA were investigated, while water absorption capacity, migration with food stimulants, water vapor permeability and antioxidant properties were tested taking into account the final application as food packaging systems. Morphological investigations evidenced homogeneity of all PVA/HTyr films, while the presence of HTyr clearly accounted for an increase… More >

Louis C. Muller^1*, Sanette Marx¹, Hermanus C.M. Vosloo²

Journal of Renewable Materials, Vol.5, No.1, pp. 67-80, 2017, DOI:10.7569/JRM.2016.634130

Abstract This work reports a study of polyol synthesis through liquefaction of technical lignins in crude glycerol by means of 1H and 31P NMR spectroscopy. The polyols are intended for preparation of polyurethane foam; thus, it is important to know how different lignin types as well as crude glycerol influence and contribute to the final polyol hydroxyl contents. Polyols prepared from organosolv lignin, kraft lignin and lignosulphonate had hydroxyl numbers suitable for rigid foam of 435, 515 and 529 mgKOH/g, respectively. The polyols differed in composition with glycerol, showing significant variation. During liquefaction the glycerol content was mostly reduced through bonding… More >

Ananda S. Amarasekara^*, Muhammad A. Hasan, Eve Larkin

Journal of Renewable Materials, Vol.5, No.1, pp. 62-66, 2017, DOI:10.7569/JRM.2016.634129

Abstract Condensation polymerization of renewable resources-based monomers, 4-ketopimelic acid and glycerol, were studied using two different catalysts; p-toluenesulfonic acid and Sb2O3. The highest polymer yield of 96% was achieved by using a 3:4 mole ratio mixture of 4-ketopimelic acid and glycerol, with Sb2O3 (0.5 mol% relative to 4-ketopimelic acid) as catalyst and heating at 23–210 °C, under N2 for 1 h; then 210 °C, vacuum, 12 h. The poly(4-ketopimelic acid-glycerol) formed is insoluble in all common organic solvents and is shown to contain a branched polymeric structure with ketal and ester links by using FT-IR, 1H and 13C NMR spectroscopy. More >

Abha Dubey^1*, Anuradha Mishra²

Journal of Renewable Materials, Vol.5, No.1, pp. 54-61, 2017, DOI:10.7569/JRM.2016.634127

Abstract Biosorption effectively removes heavy metal ions by using inexpensive biosorbents. In this study, Portulaca oleracea plant waste biomass was used as environmentally friendly biosorbent for the removal of copper ions from aqueous solution. This article includes the study of the effects of various important parameters on the biosorption process. Maximum biosorption was found to occur under slightly acidic conditions (pH 6). Small particle size, moderate agitation speed, and moderate temperature favor the biosorption process. The Langmuir model was most suitable, showing the biosorption capacity to be 85.470 mg/g. Pseudo-secondorder model best described the kinetics of the biosorption process. Thermodynamic studies… More >

María Cecilia Basso^1*, Antonio Pizzi^1,2

Journal of Renewable Materials, Vol.5, No.1, pp. 48-53, 2017, DOI:10.7569/JRM.2016.634124

Abstract New aldehyde-free and isocyanate-free biofoams have been obtained by reacting albumin chicken egg white and dimethyl carbonate (DMC). The optimized formulations yielded lightweight foams whose densities were evaluated as 0.016–0.16 g/cm3. Mechanical resistance was 0.023–0.34 MPa and residual pH nearly neutral. The new foams presented up to 57% of closed cells as measured by helium pycnometry and good thermal insulation. These new natural foams are environmentally friendly materials and show very promising properties. More >